0.25" Aluminum Hex Bar 2011-T3-Cold Finish -Part #: 7977

aluminum-hex-bar-2011-t3-cold-finish-main

FREE MTR AVAILABLE

FULL
LENGTHS

See what other people are making with this product in our gallery section >

Dimension(s) for this product

Across Flats: 0.25"

We carry 7 additional available dimensions for Aluminum Hex Bar 2011 T3 Cold Finish

Material Meets These Standard(s): ASTM-B211, AMS-QQ-A-225/3
Read More Specifications See Product Guide

Select length below or Custom Cut

12" (1 ft.) - $3.84
wt. 0.07 lb.

24" (2 ft.) - $3.62
wt. 0.14 lb.

36" (3 ft.) - $5.04
wt. 0.21 lb.

48" (4 ft.) - $5.96
wt. 0.28 lb.

72" (6 ft.) - $8.29
wt. 0.42 lb.

96" (8 ft.) - $12.16
wt. 0.56 lb.

144" (12 ft.) - $16.58
wt. 0.84 lb.

Custom Cut - Select For Price

Update Your Quantity and Add to Your Cart

QTY

$3.84 ea.

$3.84 for 1

OVERVIEW SPECIFICATIONS AND TECHNICAL INFORMATION

See Aluminum Tolerances

1/4 inch Aluminum Hex Bar 2011-T3 is easily machined, average strength, and easily given a good surface finish. 2011 is optimally suited to parts that require lots of complex machining, but aren't necessarily as reliant upon high strength or corrosion resistance. 2011 is typically used for high precision projects, such as screw machines, cameras, clocks, precision gears, and speedometers.

Dimension Name	Specification
Alloy	2011
Temper	T3
Production Method	Cold Finish
Max Length	144
Across Flats	0.25
MTR Availability	Yes
Full Length	true
Material	Aluminum
Shape	Bar-Hex
Custom Cut Warehouse	1

Material Specifications

This material meets the following specs: ASTM -B211, AMS -QQ-A-225/3

Weight/Lineal Foot
0.07 pounds

Please note that this data is to be used ONLY FOR REFERENCE, NOT FOR DESIGN, and by using it,you agree that any decisions you make regarding materials for your project are at your own discretion.

Mechanical Properties
Property	Value
Brinell hardness 500 kg load	95 min
Elongation 1/2"" thick sample	15
Endurance limit Based on 500,000,000 cycles of completely reversed stress using the R.R. Moore type of machine and specimen	18
Modulus of Elasticity Average of tension and compression moduli. Compression modulus is about 2% greater than tension modulus	10
Ultimate Tensile Strength	55
Shear Strength	32
Yield	43